Natural mica powder and synthetic mica powder have differences in production methods, heat resistance and color transparency. As the name suggests, natural mica powder is made from natural mica ore after processing, retaining the original characteristics and composition of the ore. Its main components are SiO2 (about 49%) and Al2O3 (about 30%), while also containing K2O+Na2O (9%-11%) and so on. The synthetic mica powder (such as fluoroglogopicite powder), is the use of a variety of raw materials through high temperature reaction and other chemical methods synthetic, its composition and characteristics can be adjusted and optimized according to the need, the chemical formula is KMg3(AlSi3O10)F2, belongs to the monoclinic crystal system, is a typical layered silicate, relatively single and pure composition. The heat resistance of natural mica powder is generally 500-600℃, and some types, such as phlogopite, can reach 800℃. The heat resistance of synthetic mica powder is more excellent, and it can withstand high temperatures above 1200℃, and the melting point or crystallization temperature is about 1375±5. The transparency of natural mica powder is relatively low, and the color is diverse, including black, yellow, white, gray, green, brown and other colors, and may vary due to different ore types and processing methods. The color of synthetic mica powder is relatively single, usually colorless transparent or white, high whiteness, good optical performance, and high transmittance from ultraviolet to infrared band.

The mica powder of HUAJING has the advantage of extremely narrow particle size, and the particle size specifications are complete, such as: 2000 mesh, 1250 mesh, 800 mesh, 400 mesh, 120 mesh, etc. The skin feeling is exquisite.

X represents large interlayer cations, such as K+, Na+, Ca2+, Ba2+, Rb+, Cs+, etc. Y represents octahedral cations, such as Al3+, Fe2+, Mg2+, Cr3+, Ti4+, Fe3+, etc. Z is mainly Si4+ and Al3+; The ideal ratio of the additional anion (OH)- to (O)2- is 2:10, and (OH)- can be replaced by F- and Cl-. Most mica contain 4% to 5% water. Therefore, although they may be called mica, the chemical composition of different mica may be very different, for the purpose of research, we collectively refer to the minerals with this type of characteristics as mica group minerals.  

In recent years, the beauty industry has witnessed a remarkable transformation, with innovative products and formulations captivating consumers worldwide. One of the standout trends in cosmetic development is the use of pearlescent pigments. These unique pigments have become essential in creating products that not only enhance beauty but also offer an experience that transcends traditional makeup.

X { Y2-3 [Z4O10] (OH)2 }

2. Color Variety Natural mica-based pigments are available in a wide array of colors, ranging from vibrant hues to subtle pastels. The color variations arise from the different metal oxide coatings used in the pigments, allowing manufacturers to tailor the pigments to specific needs.

The common characteristics of mica group minerals are: layered silicate minerals, monoclinic crystal system, a few trigonal crystal system, the crystals are pseudo-hexagonal columnar, plate and sheet; The aggregate is scaly and foliaceous. It has a set of extremely complete cleavage, along which it is easy to peel into sheets. Therefore, the shape of mica is usually regarded as sheet.

In conclusion, mica glitter is more than just a decorative element in lip gloss; it represents an evolution in beauty culture, blending aesthetics with ethical considerations. As consumers continue to express their individuality through makeup, the demand for products that combine beauty with responsibility will likely grow. Brands that embrace mica glitter in their formulations not only enhance the visual appeal of their products but also play a significant role in shaping the future of the beauty industry.

Take pearlescent pigments as an example, pearlescent pigments are a class of pigments with pearl luster, which are deposited on the substrate (generally natural mica, synthetic mica, glass sheet and other sheet-like materials) above a layer or alternately deposited multiple layers of metal oxides or non-metallic oxides and formed a flat sandwich body with a structure similar to sandwich. Due to the difference in refractive index between the substrate and the oxide deposited on its surface and each oxide, when the light shines on the surface of the pearlescent pigment, the incident light will be refracted and reflected at the interface of each layer of the pearlescent pigment, and the color of the pearlescent pigment that people see is the result of the superposition of light after multiple refractions and reflections of the light, that is, the interference phenomenon of light.